Influence of surface roughness and annealing on the structural, optical, electrical, and magnetic properties of Co40Fe40Dy20 thin films deposited on glass substrate

This study investigates Co40Fe40Dy20 thin films on glass substrates with thicknesses ranging from 10 nm to 50 nm under four conditions: as-deposited, annealed at 100 °C, 200 °C, and 300 °C. X-ray diffraction (XRD) confirms film amorphousness due to limited thermal energy. Maximum low-frequency alternate-current magnetic susceptibility (χac) is observed at thicker films and higher annealing temperatures, with films at 300 °C showing the highest value 0.41. Annealing at 200 °C yields exceptional properties high saturation magnetization (Ms) 748 emu/cm³ and low coercivity (Hc) 10 Oe, though Ms decreases at 300 °C due to thermal effects. Electrical resistivity and sheet resistance decrease with thickness and annealing, enhancing carrier transport. Transmittance (%) decreases notably with increased thickness, attributed to thickness and interface effects. Variations in surface roughness from annealing affect properties, with smoother surfaces improving carrier conductivity but reducing optical transparency. Overall, Co40Fe40Dy20 exhibits excellent soft magnetic properties suitable for various applications.