SHIH-HUNG LIN2026-10-162026-10-162021-06-15Pure ID: 14967692Pure UUID: 35b469d9-30a3-4aa8-80c6-e559a8c9388410.1016/j.ceramint.2021.02.256https://www.scopus.com/pages/publications/85102259610https://scholars.csmu.edu.tw/handle/123456789/31378Solid solution Ca0.6(La1-xYx)0.2667TiO3 dielectric ceramic systems with various x values were studied, which were prepared using a solid-state reaction method. X-ray diffraction and X-ray spectroscopy analyses showed that the crystal structure of these samples was orthorhombic perovskite. The microstructures with the substitution amount of Y3+ and the dielectric performances of the Ca0.6(La1-xYx)0.2667TiO3 ceramics were also explored. With x = 0.1, the Ca0.6(La0.9Y0.1)0.2667TiO3 ceramic could be sintered at 1350 °C, and the microwave dielectric performance was found to be strongly correlated with the sintering temperature. A maximum Qf value of 23,100 (GHz), dielectric constant (εr) of 111, and temperature coefficient (τf) of 374.6 ppm/°C were achieved for samples sintered at 1350 °C for 4 h. This dielectric ceramic possessed good potential as a τf compensator to obtain a near-zero τf mixture for high-quality substrates for use in wireless communication systems.5enjournal article